Ford Galaxy / Ford S-MAX. Manual - part 1081

Paint - General Information - Additional 
Materials

S-MAX/Galaxy 2006.5 (02/2006-)

 

Print

 

Description and Operation 

The manufacturer's instructions must always be followed when dealing with any 
materials! The information given in the following text is data which is independent of the 
manufacturer, and it should only used as an indication. 

Adhesive sealants 

Adhesive sealants are permanently elastic, long-lived, can be painted and accept filler.  

Application: Sealing of visible and normal seams. 

Can be over-painted with 2-component paint, primer and fillers after having dried 
throughout. 

Contamination can be removed using cleaner and thinner. 

1-component PUR adhesive sealant 

Note: 

Hardens using oxygen from the air. For that reason, it must only be stripped after it has 
completely dried through. 

2-component MS polymer adhesive sealant 

2-component MS polymer adhesive sealant is free of isocyanate, solvent and silicones and 
can be spot-welded.  

MS polymer adhesive sealant 

Can be over painted with water-based paints. 

Suitable for spraying and brushing to obtain a composition true to the original.  

MS polymer adhesive sealant is free of isocyanate, solvent and silicones and can be spot-
welded.  

Underbody protection 

Underbody protection products are immune to abrasion, permanently elastic, adhere well 
and are suitable for a true to original texture.  

Underbody protection based on solvent 

Application: 

Underbody protection for visible areas. 

Properties: 

Can be over-painted, also with 2-component paint.  
Can be colored with a proportion of up to 40% paint. 

Note: 

Contamination can be removed using cleaner and thinner. 

Water based underbody protection 

Can be over-painted with water based paint. 

Can be colored with water based paint. 

Contamination can be removed using water. 

Paint additives  

Maintain maximum layer thickness without fail. 

Must always next be overpainted with clear lacquer. 

Cannot be used in all paints, read the manufacturer's instructions.  

Particularly suitable for partial painting. 

Application

Water based underbody protection

Use

Underbody protection for visible areas

Spray viscosity

ready to use

Spray gun

Suction beaker HVLP gun 3 - 4 mm

Spray pressure

4 - 6 bar

Layer thickness

500 - 1000 µm

Drying

approx. 6 hours at 20°C 

approx. 45 - 60 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

Application

Water based underbody protection

Use

Isolation primer for peroxide marks, bloomed old paintwork and 

thermoplastics.

Spray viscosity

Thin as necessary with distilled water 

Spray gun

HVLP gun 1.9 mm

Spray pressure

2.0 - 3.0 bar

Layer 

thickness

40 - 50 µm

Drying

approx. 2 hours at 20°C 

approx. 30 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

Application

Sanding test color

Use

To test sanding results

Spray gun

HVLP 1.7 - 1.9 mm

Spray pressure

2.0 bar

Layer thickness

Spray drifted

Application

Fixer additive

Use

Converts solid top coat into two layer solid; multicolor painting

Spray viscosity

18 - 20 secs at 20°C 

Spray gun

HVLP 1.2 - 1.3 mm

Spray pressure

2.0 - 3.0 bar

Layer thickness

max. 30 µm

Coat application

Wet on wet

Ventilation time

approx. 15 - 30 minutes

Application

Drying accelerator

Use

Accelerates drying with only minimal reduction in working life

Working life

approx. 5 hours at 20°C 

Spray gun

HVLP 1.2 - 1.3 mm

Spray pressure

2.0 bar

Layer thickness

50 - 70 µm

Drying

approx. 6 hours at 20°C 

approx. 25 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

CAUTION: Do not dry using infrared. 

Note: 

When mixing, first put in the matting additive, then the hardener and thinners.  
Stir immediately after adding the matting additive.  
Do not store after addition of the matting additive, storage will change the degree of 
gloss.  
Also suitable for use on plastics without addition of elastifier additive. 

Application

Elastifier additive in primer material

Use

Elastifies the complete paint structure on plastics.

Addition

Up to 25%

Spray gun

HVLP 1.7 - 1.9 mm

Spray pressure

2.0 - 3.0 bar

Layer thickness

50 µm

Drying

approx. 4 hours at 20°C 

approx. 40 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

Application

Elastifier additive in top coat 

Use

Elastifies the complete paint structure on plastics.

Addition

Up to 25%

Spray gun

HVLP 1.7 - 1.9 mm

Spray pressure

2.0 - 3.0 bar

Layer thickness

50 - 60 µm

Drying

approx. 16 hours at 20°C 

approx. 45 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

Application

Matting additive in solid paint

Use

Elastifies the complete paint structure on plastics.

Semi-gloss addition

Up to 25% in the paint without hardener and thinner

Silk gloss addition

Up to 35% in the paint without hardener and thinner

Silk matt addition

Up to 45% in the paint without hardener and thinner

Spray gun

HVLP 1.2 - 1.3 mm

Spray pressure

2.0 - 3.0 bar

Layer thickness

50 - 70 µm

Drying

approx. 8 hours at 20°C 

approx. 30 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

Application

Matting additive in clear lacquer

Use

Elastifies the complete paint structure on plastics.

Semi-gloss addition

Up to 25% in the paint without hardener and thinner

Silk gloss addition

Up to 35% in the paint without hardener and thinner

Silk matt addition

Up to 45% in the paint without hardener and thinner

Spray gun

HVLP 1.2 - 1.3 mm

Spray pressure

2.0 - 3.0 bar

Layer thickness

50 - 70 µm

Drying

approx. 8 hours at 20°C 

approx. 30 minutes at 60°C

Application

Matting paste

Note: 

The paint must not be filtered. 

Note: 

Only add away from the paint cabin and immediately remove contaminated cloths.  
If anti-silicone additive is used in the first coat, then it must be used in the following 
coats, and in at least the same proportions. 

Additive materials 

Variety of adhesive tapes 

For profile, fine and large area masking work. 

Properties: 

Withstands heat.  
Withstands water-based paint.  
Accepts paint.  
Easily removed without leaving adhesive residues. 

Masking film. 

For masking of large areas on vehicles.  

Properties: 

Accepts 2-component and water-based paints.  
Withstands heat.  
Withstands water spray and condensation.  
Withstands solvent.  
Easily cut.  
Environmentally friendly and can be recycled. 

Polishing materials. 

Polishing means microfine sanding. For this reason, polishes must only contain abrasives, 
and no silicones. 

During polishing repair, a good shine is achieved through the step-by-step use of polishes, 
starting with a highly abrasive polish and ending with a polish having very slight abrasive 

Use

Matts, elasticizes and gives structure to solid paint and clear lacquer during 

painting of bumpers or hard plastic.

Addition

1:1 or 2:1 depending on manufacturer in solid paint without hardener or 

thinners.

Spray gun

HVLP 1.2 - 1.3 mm

Spray 

pressure

2.0 - 3.0 bar

Layer 

thickness

50 - 70 µm

Drying

approx. 6 - 10 hours at 20°C 

approx. 30 minutes at 60°C

Short wavelength infrared approx. 8 minutes

Medium wavelength infrared approx. 10 - 15 minutes

Application

Anti-silicone additive

Use

Prevents silicone craters

Addition

2% to maximum 5%