Mazda 6. Manual - part 421

PLASTIC BODY PARTS 

VI–7

VI

4. Sand the surface of the polypropylene gradually as it is easily melted by the abrasion heat. Sand the area to 

which repair agent will be applied.

5. Uniformly apply polypropylene primer with a brush to an area larger than the repaired area. Allow to dry about 

10 minutes at 20 

°C {68 °F}.

6. Mix the main agent and the stiffening agent in a ratio of one to one. Apply the mixed repair agent to the 

damaged area.

Note

• When mixing the main and stiffening agents, take care not to allow bubbles to form.

• The repair agent hardens quickly (about 5 minutes); proceed with the work immediately after mixing the 

agents.

• Allow about 30 minutes to dry (20 °C {68 °F}) before sanding.

The repair agent is a two part epoxy adhesive.
When the repair agent hardens, it will provide a good finish with the same flexibility as the polypropylens.
The repair agent for a urethane bumper is also a two part adhesive compound. However, this is different from 
that for a polypropylene bumper. If the incorrect repair agent is used, the repair will be faulty.

YMU980PCX

YMU980PCY

YMU980PCZ

VI–8

PLASTIC BODY PARTS 

7. Sand the area with #180—240 sandpaper.

Note

• If excessive force is applied to the area when sanding, the surface will be damaged.

• If fuzz remains around the repaired area, melt it with a heat gun.

8. Degrease the painted surface.
9. Mix the primer and the hardener at a ratio of one to one. Apply the primer to the repaired area and the surface 

of the bumper with a brush or spray.

Use the primer within 16 hours after it is mixed.

Note

• Polypropylene primer will dissolve even after drying if it is wiped with solvent. Use only water to clean 

around the primer.

10. Allow the part to dry.

YMU980PD0

YMU980PD1

PLASTIC BODY PARTS 

VI–9

VI

11. Add the softener to the urethane primer surfacer and spray it on the repaired area.

a. Mixing method

Urethane primer surfacer + Softener..... Mixture A
Mixture A + hardener..... Mixture B
Dilute mixture B with thinner to spray on bumper

b. Viscosity

14—16 seconds/viscosimeter 20 

°C {68 °F}

Note

• Mix the solutions at the specified ratio.

c. Spray pressure

300—400 kPa {3—4 kgf/cm

2

, 43—57 psi}

d. Standard film thickness

30—40 

µ

e. Spray method

Spot-spray primer surfacrer on bumper three of four times

12. Air drying 20 

°C {68 °F} — 8 hours minimum.

Forced drying 60 

°C {140 °F} — 1 hour

13. Lightly sand the complete surface of the bumper with #400—#600 sandpaper. Do not expose the surface of the 

polypropylene. (Wet or dry sanding is acceptable.)

14. Wipe the complete surface of the bumper with degreasing agent. Quickly wipe the surface with a clean rag to 

degrease it.

15. Apply a matching coat of body color to the polypropylene bumper.

Note

• Be sure to use only urethane primer for a urethane bumper and polypropylene primer for a polypropylene 

bumper. Other paints for repairing a polypropylene bumper are the same as those for the urethane 
bumper.

16. Air drying 20 

°C {68 °F} — 8 hours minimum.

Forced drying 60 

°C {140 °F} — 1 hour

Note

• Let the part air dry when possible as forced drying could cause bubbles in the top coat.

End Of Sie

YMU980PD2

VII–1

VII

VII

PRIMARY COLOR MIXTURE CHART FOR 

BODY COLORS

PRIMARY COLOR MIXTURE CHART FOR 

BODY COLORS ................................................ VII-2
PRIMARY COLOR MIXTURE CHART FOR 

BODY COLORS.............................................. VII-2