Ford Fiesta (2011 year). Manual - part 172

2-component polyester

glass fiber stopper

Application

approx. 4 - 6 minutes

Working time

20°C approx. 12 minutes

Drying

Short wavelength infrared

approx. 4 minutes

Medium wavelength

infrared approx. 5 - 10

minutes

Eccentric, sanding disk

by hand

Sanding tool

P80 - P150

Grade

2-component polyester fine stopper should always
be applied after 2-component polyester glass fiber
stopper.

2-component polyester

spray stopper

Application

Equalization of uneven-

ness

Use

approx. 3 - 5%

Hardener quantity

approx. 25 - 30 minutes

Working time

200 µm or 4 - 8 spray

passes

Layer thickness

20°C approx. 3 hours

Drying

Short wavelength infrared

approx. 10 minutes

Medium wavelength

infrared approx. 15 - 20

minutes

Eccentric, sanding disk

by hand

Sanding tool

P80 - P150; fine sand -

P280

Grade

2-component plastic

stopper for flexible

thermoplastic

Application

Equalization of scratches

or unevenness

Use

approx. 3 - 5%

Hardener quantity

approx. 25 - 30 minutes

Working time

20°C approx. 15 - 30

minutes

Drying

2-component plastic

stopper for flexible

thermoplastic

Application

60°C approx. 15 min

(Short wavelength

infrared approx. 8

minutes)*

(Medium wavelength

infrared approx. 8-10

minutes)*

Eccentric, sanding disk

by hand

Sanding tool

P80 - P150; fine sand -

P280

Grade

*Infrared drying may adversely affect adhesion,
therefore check the manufacturer's
instructions.

Plastic stopper has a very great tendency to shrink
back, so that the edge of the stopper repair
becomes visible.

Plastic stoppers are flexible and universally
applicable on all types of plastic (except for pure
PE and PP, these are plastics which cannot be
painted). The manufacturer's instructions must be
very exactly followed in order that no adhesion
problems occur. A special plastic etch primer is
specified for some materials.

Primers

1-component primer

Application

Isolation of bare sanded

areas.

Use

HVLP 1.3 mm

Spray gun

2.0 bar

Spray pressure

20°C approx. 15 - 20

minutes

Drying

60°C approx. 10 min

Wet on wet, no interme-

diate sanding

Coat application

2-component primer

Application

Corrosion protection and

bonding agent (steel

sheet, zinc coated steel

sheet, aluminum)

Use

G468096en

501-36-

36

Paint - General Information

501-36-

36

DESCRIPTION AND OPERATION

201

2-component primer

Application

HVLP 1.3 mm

Spray gun

2.0 bar

Spray pressure

20°C approx. 15 - 20

minutes

Drying

60°C approx. 10 min

Wet on wet, no interme-

diate sanding

Coat application

HS primer filler and HS tinted filler

Note:

• Primer filler is available as 1-component and

2-component water based and solvent based
forms.

• 1-component products are only suitable for

isolation of sanded through bare areas and new
painting.

• Water based products are also used for the

skinning of thermoplastics and substrates which
are sensitive to solvents.

• Tinted fillers can be individually matched to the

top coat color and therefore find uses in effect
paints and paints with poor covering power.

• Use dry sand or wet sand filler according to

application in order to avoid unnecessary
sanding work.

• On critical substrates the use of epoxy resin

base filler is recommended in order to avoid
adhesion problems.

HS primer filler and HS

tinted filler

Application

Equalization of uneven-

ness, edge zones,

sanding scores

Use

HVLP 1.6 - 1.9 mm

Spray gun

2.0 bar

Spray pressure

50 - 70 µm to 150 µm

possible

Layer thickness

20°C approx. 2.5 hours

Drying

(60°C approx. 25 min)*

(Short wavelength

infrared approx. 8

minutes)*

HS primer filler and HS

tinted filler

Application

(Medium wavelength

infrared approx. 10-15

minutes)*

Wet on wet, no interme-

diate sanding

Coat application

*In order to avoid boiling out, drying should be
performed slowly.

Paint

The base and the clear lacquer must be matched
to one another.

Water based paint

Application

Two layer metallic effect

paint and Uni-paint

finishes

Use

At 20°C 18 - 20 s

Spray viscosity

HVLP 1.2 - 1.3 mm

Spray gun

2.0 bar

Spray pressure

15 - 20 µm

Layer thickness

20°C approx. 2.5 hours

Drying

60°C approx. 25 min

Short wavelength infrared

approx. 8 minutes

Medium wavelength

infrared approx. 10 - 15

minutes

Wet on wet

Coat application

approx. 5 minutes

Ventilation time

The base paint must be dried matt before the clear
lacquer is applied.

2-component HS clear

lacquer

Application

Gloss providing

protective coat for base

coat substrate

Use

At 20°C 18 - 20 s

Spray viscosity

HVLP 1.2 - 1.3 mm

Spray gun

2.0 bar

Spray pressure

50 - 70 µm

Layer thickness

G468096en

501-36-

37

Paint - General Information

501-36-

37

DESCRIPTION AND OPERATION

201

2-component HS clear

lacquer

Application

20°C approx. 10 hours

Drying

60°C approx. 30 min

Short wavelength infrared

approx. 8 minutes

Medium wavelength

infrared approx. 10 - 15

minutes

2K HS Uni top coat

Application

Color and gloss providing

paint layer

Use

At 20°C 20 - 22 s

Spray viscosity

HVLP 1.2 - 1.3 mm

Spray gun

2.0 bar - 3.0 bar

Spray pressure

50 - 70 µm

Layer thickness

20°C approx. 8 hours

Drying

60°C approx. 30 min

Short wavelength infrared

approx. 8 minutes

Medium wavelength

infrared approx. 10 -15

minutes

G468096en

501-36-

38

Paint - General Information

501-36-

38

DESCRIPTION AND OPERATION

201

Additional Materials

The manufacturer's instructions must always
be followed when dealing with any materials!
The information given in the following text is data
which is independent of the manufacturer, and it
should only used as an indication.

Adhesive sealants

Adhesive sealants are permanently elastic,
long-lived, can be painted and accept filler.

Application: Sealing of visible and normal seams.

Can be over-painted with 2-component paint,
primer and fillers after having dried throughout.

Contamination can be removed using cleaner and
thinner.

1-component PUR adhesive sealant

Note:

• Hardens using oxygen from the air. For that

reason, it must only be stripped after it has
completely dried through.

2-component MS polymer adhesive sealant

2-component MS polymer adhesive sealant is free
of isocyanate, solvent and silicones and can be
spot-welded.

MS polymer adhesive sealant

Can be over painted with water-based paints.

Suitable for spraying and brushing to obtain a
composition true to the original.

MS polymer adhesive sealant is free of isocyanate,
solvent and silicones and can be spot-welded.

Underbody protection

Underbody protection products are immune to
abrasion, permanently elastic, adhere well and are
suitable for a true to original texture.

Underbody protection based on solvent

Application:

• Underbody protection for visible areas.

Properties:

• Can be over-painted, also with 2-component

paint.

• Can be colored with a proportion of up to 40%

paint.

Note:

• Contamination can be removed using cleaner

and thinner.

Water based underbody protection

Can be over-painted with water based paint.

Can be colored with water based paint.

Contamination can be removed using water.

Water based underbody

protection

Application

Underbody protection

for visible areas

Use

ready to use

Spray viscosity

Suction beaker HVLP

gun 3 - 4 mm

Spray gun

4 - 6 bar

Spray pressure

500 - 1000 µm

Layer thickness

approx. 6 hours at 20°C

Drying

approx. 45 - 60 minutes

at 60°C

Short wavelength infrared

approx. 8 minutes

Medium wavelength

infrared approx. 10 - 15

minutes

Water based underbody

protection

Application

Isolation primer for

peroxide marks, bloomed
old paintwork and thermo-

plastics.

Use

G468097en

501-36-

39

Paint - General Information

501-36-

39

DESCRIPTION AND OPERATION

201